WD1000/1100 Wear Plate
WD1000/WD1100 series
Abrasion Resistant Chromium Carbide Overlay
1111MicrosoftInternetExplorer402DocumentNotSpecified7.8 磅Normal0
WD1000/WD1100 is chromium carbide composite cladding fusion bonded to a mild steel backing plate. The deposit has been realized by means of flux cored arc welding. WD1000/WD1100 wear plate is suitable for application involving high abrasion and low to medium impact.
● WD1000/WD1100 series:
Common chromium carbide wear plates produced by flux cored arc welding; Suited for applications involving high abrasion and low to medium impact.
|
Chemicals |
Hardness |
Sheet Size |
Base Metal |
|
C – Cr – Fe |
HRC 58-63 |
1400*3400 |
Q235/Q345. etc |
| Chemical Composition(%) |
C |
Cr |
Mn |
Si |
Fe |
Other |
|
3.0-5.0 |
15.0-35.0 |
1.0-3.0 |
1.0-3.0 |
Bal. |
- |
|
| Hardness |
HRC 58-65 |
|||||
| Standard Thickness(mm) |
3+3; 4+4; 5+5; 6+4; 6+6; 8+4; 8+6; 8+8; 10+10; 12+12; etc (overlay thickness up to 50mm) |
|||||
| Standard Sheet Size(mm) |
1400*3400; 1500*3000; 2000*3000; (Customized size available) |
|||||
| ASTM G65 Procedure A |
0.12 – 0.18g |
|||||
| Operating Temperature |
<400 ℃ |
|||||
| Base Metal Material |
Q235B, Q345B; A36; S235JR and structural steels |
|||||
| Main Industry |
Mining, glass industry, cement plant, steel mill, power plant, etc |
|||||
| Fabrication |
Plasma cutting, Gouging, Countersunk, stud bolt, Bending |
|||||
We can customize the plates in different sizes and thickness based on customer’s drawings. we can also cut, bend and weld the wear plates into specific shapes and parts
Characteristics:
- * Chromium carbide overlay wear resistant plate
* Chemical Composition: C: 3.0-5.0% Cr: 18-30%
* Chromium carbide Cr7C3 volume fraction about 40%
* The thickness of wear resistant layer can reach up to 50 mm
* Heat resistance up to 600°C
* Lager standard wear resistant area 1400*3400mm, 1500*3000mm, 2000*3000mm
* Better flatness with smooth surface
* Hardness: HRC58-65